2KAS HYBRID STP

ADHESIVE 65E100.

 

 

Skin / Gel

Handling time

Cure time

Skin formation time

Density

Shore A hardness

Modulus at break

100% elongation at break

Shear strength wood/wood

Dry matter content

Processing temperature

Temperature stability

Moisture resistance

Frost resistance

Mixing ratio

 

 

10-15 mins

1 hrs

6 hrs

10-15 mins at 23°C and 50% R.H.

1.58 g/mI approx

65 (+/- 5) (ISO-868)

3.500 N/mm2 (ISO-37)

>100% approx

2.5 N/mm2 (after 8hrs curing)

100% approx

+5°C to +40°C (do not process below +5°C)

-40°C to +90°C

very good

not sensitive to frost

10:1 (two component)

2KAS HYBRID STP ADHESIVE 65E100 IS A HIGH QUALITY TWO COMPONENT, FAST CURING ELASTIC ADHESIVE SEALANT BASED ON HYBRID POLYMERS.

 

It has a very fast build-up of internal strength and assembled parts can be handled relatively quickly after bonding.

 

2KAS hybrid STP Adhesive 65E100 bonds without primer aluminium, galvanized and stainless steel, zinc, copper, natural stone, concrete, brick, cement based cover sheeting, HPL panels, treated wood, gypsum, glass, glazing and fibre glass synthetic materials.

 

Available in the unique CiC packaging systems

Easy to use

Always the correct mixing ratio (when supplied in a cartridge)

Can be used on damp concrete

Shrink resistant

Non-sagging (vertical overhead applications)

 